PENGUJIAN METALLOGRAPHY MATERIAL AISI 430 SUDU KINCIR AIR DENGAN HEAT TREATMENT DAN TANPA HEAT TREATMENT
DOI:
https://doi.org/10.56127/juit.v2i2.786Keywords:
Heat Treatment, Waterwheel, MetalloraphyAbstract
Metallography testing aims to be able to observe the microstructure. The steps that must be passed are preparing the test sample by cutting the specimen, mounting, sanding, polishing and etching. In material specimens without heat treatment, the results of the microstructure of ferrite and pearlite were obtained, with the conclusion that Ferrite is ferromagnetic up to temperature and is ductile, Pearlite is the result of a eutectoid reaction. The faster the cooling rate, the finer the grain and the better the mechanical properties of the steel. Explanation of the phases of material specimens with heat treatment. The difference from specimens without heat treatment is the formation of a bainite phase. This bainite phase was formed due to heat treatment which was carried out for 1 hour at 550⁰C. The quenching process using oil greatly influences the results of the formation of the bainite phase, because oil has better heat absorption properties. The conclusion of this paper is the difference in the microstructure of material specimens without heat treatment and specimens with heat treatment. In the specimen without heat treatment, two ferrite phases and a pearlite phase were obtained. while the heattreated specimens yielded three ferrite, pearlite and bainite phases. This bainite phase was formed due to heat treatment with a temperature of 550⁰C for 1 hour.
References
M. I. Almadani and R. Siswanto, “PROSES MANUFAKTUR MESIN POLES DAN AMPELAS UNTUK PROSES METALOGRAFI,” JTAM ROTARY, vol. 2, no. 1, 2020, doi: 10.20527/jtam_rotary.v2i1.2001.
S. Sukamta and A. Kusmantoro, “Perencanaan Pembangkit Listrik Tenaga Mikro Hidro (PLTMH) Jantur Tabalas Kalimantan Timur,” J. Tek. Elektro Unnes, vol. 5, no. 2, pp. 58–63, 2013.
F. A. Putra, “ANALISA PENGARUH SUDUT SUDU DAN DEBIT ALIRAN TERHADAP PERFORMA TURBIN KAPLAN,” BMC Public Health, vol. 5, no. 1, 2018.
S. Armansyah, “Pengaruh Penguatan Medan Generator Sinkron Terhadap Tegangan Terminal,” J. Tek. Elektro UISU, vol. 1, no. 3, 2016.
Y. Watanabe, H. Abe, and Y. Oka, “Materials,” Supercrit. Light Water Cool. React., vol. 9784431550, pp. 321–345, 2014, doi: 10.1007/978-4-431-55025-9_4.
S. A. Yudistirani, K. H. Mahmud, and E. Diniardi, “Analisis Kekerasan Pada Outer Ring Dan Inner Ring Hasil Proses Heat Treatment,” J. Teknol., vol. 10, no. 1, 2018.
D. Yuhani, M. Budhi, and Marsud, “Upn " Veteran " Jakarta Upn " Veteran " Jakarta,” Bina Widya, vol. 25, pp. 1–10, 2016.